- Research article
- Open Access
Evaluation of chitosan-GP hydrogel biocompatibility in osteochondral defects: an experimental approach
BMC Veterinary Research volume 10, Article number: 197 (2014)
Articular cartilage, because of its avascular nature, has little capacity for spontaneous healing, and tissue engineering approaches, employing different biomaterials and cells, are under development. Among the investigated biomaterials are the chitosan-based hydrogels. Although thoroughly studied in other mammalian species, studies are scarce in equines. So, the aim of the present study was to investigate the biocompatibility of chitosan-GP in horse joints submitted to high mechanical loads.
An osteochondral defect was created by arthroscopy in the medial surface of lateral trochlea of talus of left or right leg, randomly selected, from six healthy geldings. The defect was filled up with chitosan-GP. The contralateral joint received an identical defect with no implant. The chondral fragment removed to produce the defect was collected, processed and used as the "Initial" sample (normal cartilage) for histology, immunohistochemistry, and metabolic labelling of PGs. After 180 days, the repair tissues were collected, and also analyzed. At the end of the experiment (180 days after lesion), the total number of cells per field in repair tissues was equal to control, and macrophages and polymorphonuclear cells were not detected, suggesting that no significant inflammation was present. These cells were able to synthesize type II collagen and proteoglycans (PGs). Nevertheless, the cell population in these tissues, both in presence of chitosan-GP and in untreated controls, were heterogeneous, with a lower proportion of type II collagen-positives cells and some with a fibroblastic aspect. Moreover, the PGs synthesized in repair tissues formed in presence or absence of chitosan-GP were similar to those of normal cartilage. However, the chitosan-GP treated tissue had an disorganized appearance, and blood vessels were present.
Implanted chitosan-GP did not evoke an important inflammatory reaction, and permitted cell growth. These cells were able to synthesize type II collagen and PGs similar to those synthesized in normal cartilage and in healing tissue without implant, indicating its chondrocyte nature.
Injuries to articular cartilage are common, and may cause pain, disability, impairment, and early retirement of athletes. Once damaged, articular cartilage has very little capacity for spontaneous healing, and many repair techniques have been proposed over the last decades. However, repair of articular cartilage by traditional methods is challenging, due to its avascular nature and lack of a significant population of progenitor cells. For this reason, tissue engineering approaches, employing cells to in situ regenerate articular cartilage, are under development -.
Both fully differentiated chondrocytes and progenitor cells (mesenchymal stem cells) have been used to produce hyaline-like cartilage ,. Nevertheless, the strategies of cell implantation within the joint also poses challenges: a fluid environment, strong shear forces, mechanical loads, and stiff, irregular and often bleeding surfaces not easily amenable to insertion of biomaterials. Furthermore, the biomaterials to be used as cell-delivery vehicles must meet stringent requirements in that the material should be non-toxic, non-immunogenic, and must either integrate with the repair tissue or degrade without generating toxic by-products or leaving gaps, debris or fissures in the tissue . The ideal scaffold should mimic the naturally occurring environment in the articular cartilage extracellular matrix (ECM), allowing chondrocyte proliferation and synthesis of cartilage ECM, which is composed by a dense network of collagen fibers , proteoglycans (PGs), and other proteins .
PGs are composed by a protein core with glycosaminoglycan (GAG) side chains. GAGs, in turn, are heteropolysaccharides constituted by repeating disaccharide units formed by a hexosamine (glucosamine or galactosamine) and a non-nitrogen monosaccharide (uronic acid or galactose). Most GAGs are sulfated in different degrees and positions, and both the carboxyl and the sulfate groups contribute to its polyanionic nature. The main cartilage matrix PG is aggrecan, a high molecular weight PG of the hyalectan family, composed by a ~200 kDa core protein substituted with ~100 chondroitin sulfate and ~30 keratan sulfate side chains. Aggrecan interacts with hyaluronic acid, forming large aggregates, which are entrapped in the collagen network, and provide cartilage its osmotic properties, giving cartilage its ability to resist compressive loads review in . Other PGs, such as decorin, biglycan and fibromodulin, which are characterized by their ability to interact with collagen, are also present. They are much smaller than aggrecan, but may be present in similar molar amounts.
The structure and composition of aggrecan in articular cartilage changes when growth and calcification processes occur in the tissue, both during normal development and in diseases such as osteoarthritis and tumors ,. Furthermore, the extracellular matrix composition, the cell density , and even mechanical compression  affect the chondrocyte phenotype and the synthesis of ECM components. Thus, the composition of any biomaterial used as in cartilage regeneration procedures is very important.
A wide array of matrices or hydrogels have been used as biomaterials, including proteins (collagen and fibrin), polysaccharides (agarose, alginate, hyaluronic acid and chitosan), and polymers (polyethylene glycol, poly-lactic acid) . Chitosan-based hydrogels are promising due to their structural analogy to GAGs.
Chitosan is a partially deacetylated derivative of chitin, isolated from arthropod exoskeleton . It is a linear polysaccharide consisting of β (1-4) linked D-glucosamine residues, with a variable number of randomly located N-acetyl-glucosamine residues. Chitosan is a semi-crystalline polymer, and the degree of crystallinity is a function of the deacetylation level. Because of its structure, chitosan is normally insoluble in aqueous solutions above pH 7, but, in dilute acids, the free amino groups are protonated and the molecule becomes fully soluble below pH 5 .
Many chemical derivatizations of chitosan have been used to promote new biological activities and to modify its mechanical properties ,. The addition of polyol salts such as sodium glycerol phosphate to chitosan creates chitosan-glycerol phosphate (GP), a thermosensitive hydrogel that forms a viscous liquid at room temperature or below, and converts to a semisolid gel at body temperature -. Chitosan-based vehicle can be loaded into an osteochondral defect in living joints as a viscous liquid, and upon solidification, adheres to bone and to cartilage . Furthermore, previous studies have shown that chitosan is hemostatic , and stimulates revascularization of the wound and connective tissue repair .
The aim of the present study was to investigate the biocompatibility of a chitosan-based hydrogel – chitosan-GP – in horses, specifically in joints submitted to high mechanical load. If proved biocompatible in horses, chitosan-GP could be used, in the future, as a vehicle for cell and/or drug delivery as an adjuvant to promote cartilage regeneration.
The present work was approved by the Ethical Committee of Universidade de São Paulo - USP (1245/2007), and was carried out in accordance with USP guidelines, and also in accordance with EC Directive 86/609/EEC for animal experiments http://ec.europa.eu/environment/chemicals/lab_animals/legislation_en.htm.
Six Mangalarga healthy geldings, 3 years old, 300-315 kg body weight (average = 307 kg), from the USP research herd, were used in the present study. Clinical, laboratorial, radiographic and ultrassonographic exams were performed before inclusion in the experimental group, and all were considered normal. The animals were housed in single 12 m2 boxes (3 × 4 m) and fed pellets (1% of the animal body weight), coast cross hay and water ad libitum.
Preparation and application of chitosan-glycerol phosphate gel
Chitosan-GP gel was obtained as described by Chenite et al. . In brief, chitosana of 310-375 kDa (based on the viscosity range of 800-2000 mPaS) deacetylation grade >75% (200 mg), was solubilised in 0.1 m hydrochloric acid (9 mL). To this solution, 560 mg of sodium glycerol phosphateb dissolved in 1 mL of water were added, slowly and under continuous agitation. A whitish gel resulted, which was transferred to glass tubes, sterilized in autoclave, and stored for no more than 24 h at room temperature.
To test the biocompatibility of chitosan-GP, an osteochondral defect (1 cm diameter and 0.5 cm deep) was created by arthroscopy in the medial surface of lateral trochlea of talus, in left or right leg, randomly selected. A cartilage sample was collected with Ferris-Smith rongeous, and used as "Initial sample". Afterwards, a depression was created in the subjacent bone using a bone burr attached to a power shaving system. This osteochondral defect was filled up with chitosan-GP gel (~0.5 mL). The gel was delivered using an insulin syringe (1 mL), with cut end. For gel delivery, fluid infusion was replaced by CO2, using a laparoscopic insuflattor calibrated to maintain 30 mmHg until the end of the procedure, allowing gel retention in the defect. The contralateral joint received an identical defect with no implant, and served as matched control.
After arthroscopy, all horses received intravenous amikacin, 15 mg/kg, and phenylbutazone, 4.4 mg/kg, every 24 h, for three days. At the end of the experimental period (day 180), arthroscopy was repeated for the collection of the "Final" samples, and the same antibiotic and anti-inflammatory therapy was repeated.
The cartilage samples collected during arthroscopy were cut in three fragments, used for: (1) histology; (2) immunohistochemistry for type II collagen; (3) metabolic labelling and analysis of proteoglycans (PGs).
For histology, the tissue fragments were fixed in Methacarn (60% methanol, 30% chloroform, 10% acetic acid) for 6 h, and then transferred to 90% ethanol. The tissues were dehydrated, embedded in paraffin, and cut in 3 μm sections. These sections were transferred to silane-coated microscope slides, dewaxed and stained with hematoxylin and eosin (H & E).
Immunofluorescence of type II collagen
For immunofluorescence labelling, the tissue fragments were fixed as above described, dehydrated, embedded in paraffin, and cut in 5 μm sections. These sections were transferred to silane-coated microscope slides and dewaxed. Antigen retrieval was performed by incubation with 0.4% pepsin (Sigma) in 0.5 m acetic acid, 30 min, 37°C. After washing with phosphate buffering saline (PBS), polyclonal anti-type II collagen antibodyc was added as primary antibody (100 μL), 1:50 in blocking solution containing 1% bovine serum albumin, BSAd, 0.3% Tween 20 and 0.1% sodium azide. This antibody binds both type II mature collagen and procollagen. After overnight incubation at 4°C, the slides were washed with PBS and incubated with secondary antibody swine anti-rabbit IgG, FITC-conjugatede, diluted 1:100 in PBS. After 90 min incubation in moist and dark chamber, the sections were counterstained with propidium iodide (1:1000), which stains cell nucleus in red. Slides were mounted in Vectashield to preserve fluorescencef, and sealed with clear nail polish. Negative controls consisted of cartilage sections that had not been incubated with primary antibody.
Images were obtained with a Nikon E-800 fluorescence microscope, 400 times magnification, and morphometric analysis was performed using the software Image ProPlus 4.5. The evaluation consisted of counting 100 cells per sample, in random selected fields, following basic stereological principles. The results are expressed in percentage of type II collagen -positive cells.
Metabolic labelling and analysis of proteoglycans
For metabolic labelling of PGs, the cartilage fragment (~100 mg) was transferred to a sterile bottle containing 10 mL of F12 culture medium containing penicillin (10.000 U), streptomycin (100 mg) and 35S-sulfateg (100 μCi). The tissue explants were transferred to Dept. of Biochemistry, Escola Paulista de Medicina, and maintained at 37°C in a 2.5% CO2 atmosphere. After 24 h, the medium and the tissue explants were collected and processed separately.
Extraction of 35S-PGs from tissue explants
From the conditioned culture medium, the PGs were precipitated by careful and slow addition of methanol (3 volumes), and after 18 h at -20°C, the precipitate formed was collected by centrifugation, dried and resuspended in 100 μL of water for analysis.
From the tissue explants, 35S-PG extraction was performed as previously described -. Each tissue explant was carefully cut in small pieces, and incubated with 1 mL of 4 m guanidine hydrochloride (GuHCl)h in 0.05 m sodium acetate buffer, pH 6.5, containing protease inhibitors (0.1 m є-aminocaproic acid, 6.5 mM benzamidine, 5.5 mM iodocetamide and 0.1 m phenylmethylsulfonyl fluoride). After overnight incubation at 4°C under agitation, debris was collected by centrifugation, and the extraction process was repeated with 0.5 mL of the 4 m GuHCl. After 24 h, debris was removed by centrifugation and both supernatants were combined. PGs were precipitated by slow addition of methanol (3 volumes), under agitation. Subsequently, the precipitates formed after 18 h at -20°C were collected by centrifugation (3000 × g, 20 min), washed with 80% methanol, and vacuum dried. The dried material was resuspended in water (100 μL), and the solutions were stored at -20°C.
Identification and quantification of 35S-PGs
The 35S-PG samples were analyzed by a combination of agarose gel electrophoresis and enzymatic degradation with proteases and specific GAG lyases, as already described . Aliquots of the 35S-PG-containing solutions (5 μL containing 0.5-5 μg) were submitted to agarose gel electrophoresis in 0.05 m 1,3-diaminopropane-acetate buffer (PDA), pH 9 . After fixation with cetyltrimethylammonium bromide and Toluidine Blue staining, PGs were quantified by densitometry of the gel slabsi. The 35S-sulfate labelled compounds were visualized by exposure of the gel slabs to a Packard Cyclone TM Storage Phosphor System by 24 hours. For quantification, the bands containing radiolabelled compounds were scrapped from the gel slabs and counted in a liquid scintillation spectrophotometer, using Ultima Gold LSC-Cocktailj. The quantitative results were always corrected for 35S-decay.
Data were evaluated for normality by the Kolmogorov-Smirnov test. Afterwards, the Analysis of Variance was used to compare the groups and effect of treatments. To contrast between mean values the Tukey-Kramer test was used. For non-parametric values, Kruskal-Wallis test was used to compare initial and final results, while Mann–Whitney test was used to compare the chitosan-GP-treated joints to the untreated. The GraphPad Instat 3 was used to perform the statistical analysis.
Histology and immunohistochemistry of type II collagen with fluorescence labelling
Gross observation revealed that at the beginning of experiment, the articular cartilage was normal with smooth surface. At the end of experimental period (day 180), a slight depression was easily detected by arthroscopy as the lesion was observed. The surface was also smooth and cartilage-like. Histological images of the initial chondral fragment obtained by arthroscopy is shown in Figure 1 (A and B). Chondrocytes are embedded in abundant avascular ECM of homogeneous appearance upon HE staining. Figure 1-C shows that, 180 days after osteochondral injury (Final), the chitosan-GP treated tissue had an abnormal, disorganized appearance. The cells were also embedded in abundant ECM, but now blood vessels were present. In both healing tissues, some cells presented a "fibroblastic" morphology. Possibly, they are mesenchymal cells that could differenciate into either chondrocytes or fibroblasts. The total number of cells per field did not change, and macrophages and polymorphonuclear cells were not detected, suggesting that no significant inflammation was present in the "Final" samples (180 days). Similar results were obtained for all animals, and Figure 1 shows representative samples of each group.
Immunofluorescence for type II collagen was performed as described in Methods, and the percentage of type II collagen-positive cells was measured (Figure 2). Although the matrix was also labelled, our focus was the newly synthesized pro-collagen present in the cells. In normal cartilage, about 70% of the cartilage cells were type II collagen-positive, while in healing tissues this number was much lower (~40%). Nevertheless, there was no difference between healing tissues formed in presence or absence of chitosan-GP.
Representative agarose gel electrophoresis of 35S-PG extracted from cartilage explants (T) and conditioned culture medium (M), from normal tissues obtained at the beginning of experiment (Initial), and repair tissues collected at the end of experimental period (Final), from chitosan-GP-treated lesions (Chitosan-GP) and untreated lesions (No treatment) is shown in Figure 3. Both Toluidine Blue staining and radioautograms are shown. The radioactive band corresponded to the Toluidine Blue stained PGs, indicating that PGs were the main 35S-sulfate labelled compounds. Intact PGs migrated near heparan sulfate (free GAG), but upon digestion with proteases (not shown), only chondroitin sulfate free chains appeared, indication that most of the 35S-PGs synthesized are chondroitin sulfate-PGs.
Figure 4 shows the quantitative data for total PGs (stained by Toluidine Blue and quantified by densitometry) and newly synthesized, labelled PGs (35S-PGs). In all cases, most of the 35S-PGs were found in the tissue explants, with only 10-12% of total 35S-PGs in culture medium of normal tissues (Initial). Although both the total amounts of PGs (Figure 4-A) and 35S-PGs (Figure 4-B) were lower in healing tissues, a higher proportion (30-33%) was found in culture media (Figure 4-C), suggesting that the extracellular matrix was less dense than in the normal tissue. The healing tissues contained also lower amounts of PGs, detected both by Toluidine Blue staining and radioactivity.
The PG concentration in the culture medium was very low, undetectable by Toluidine Blue staining. For this reason, it was impossible to determine the specific activities of PGs secreted to the culture medium. So, only tissue explants were considered to measure specific activities. In healing tissues, although the amounts of PGs were lower than normal, the specific activities were increased (Figure 5), indicating higher synthesis rates. The specific activities were even higher in the chitosan-GP-treated lesions. Nevertheless, individual variation did occur, possibly due to different numbers of PG-synthesizing cells in each sample.
Much of the potential of chitosan as a biomaterial is thought to come from its cationic nature and high charge density. Because the chitosan charge density is pH-dependent, transfer of chitosan-polyanion complexes to physiological pH can result in dissociation of the immobilized polyanion, and this could be used for local delivery of biologically active molecules . Furthermore, the N-acetylglucosamine moiety of chitosan is also found in some GAGs, such as hyaluronic acid, heparan suphate and heparin, giving these molecules a certain degree of structural analogy. It is possible that chitosan might present some of the GAG biological activities, such as the ability to bind growth factors, receptors and adhesion molecules. However, Hamilton et al. claim that other properties may be important in biological performance of chitosan .
Many authors propose chitosan-based biomaterials for cartilage tissue regeneration, but different chitosan formulations are used. The chitosan molecular weight may range from as little as 10 kDa to over 1,000 kDa, while the deacetylation degree may oscillate from 50% to 95% . High molecular weight and high deacetylation degrees are related to lower material degradation, while the deacetylation degree is also related with cell adhesion and proliferation. In the present paper, we choose to employ an intermediate molecular weight, and a 310-375 kDa chitosan, with 75% deacetylation was used.
The chitosan primary amino groups are reactive and provide a mechanism for side group attachment using mild reaction conditions. The general effect of addition of a side group is to disrupt the crystalline structure of chitosan and hence increase the amorphous fraction, generating a material with lower stiffness and altered solubility. Chitosan-GP is one such compound , having the additional benefit of forming a thermosensitive hydrogel that forms a viscous liquid at room temperature, and converts to a semisolid gel at body temperature, making easier its application in osteochondral defects. There are strong evidences that the gelation in the chitosan-GP system induced by heating is the result of a progressive and homogeneous reduction of the ionization degree of chitosan .
Other carbohydrate-based biomaterials, such as polylactic/polyglycolic acids, agarose, and alginate, have been used, but most of them, in contrast to chitosan, give strong foreign body reactions review in .
Although thoroughly studied in humans and in experimental models reviews in ,, only a few reports on the use of chitosan-based biomaterials in equines have been published , and while the body response to various chitosan-based implants has been studied in other species ,, there are scarce studies in horses. In general, studies in other species have revealed that chitosan-based materials are biocompatible and evoke minimal foreign body reaction. Chitosan, chitosan fragments, and chitin have been shown to have short-term stimulatory effects on the immune system -, which may play a role in inducing local cell proliferation and ultimately integration of the implanted material within the host tissues. In the rabbit, it was shown that less adverse tissue response occurred with better biodegradable samples, of low molecular weight chitosan and low deacetylation degree (83%) . With high molecular weight chitosan (350-510 kDa) or high deacetylation degree (91%), however, Abarrategi et al. described synovial membrane inflammation, no cartilage formation, no material degradation, and nonsmooth surface . In contrast, our findings in horses, using chitosan-GP of 310-375 kDa and 75% deacetylation, revealed smooth surface, with a good host integration of healing tissue, and no evidence of chronic inflammation in any of our experimental animals. Blood vessels were observed in repair tissues formed in presence of chitosan-GP, as were also reported by others, who concluded that chitosan induces a transient vascularization when implanted in cartilage . In a rabbit model, chitosan-GP/blood implants induce angiogenesis and subchondral bone remodeling. These observations suggest that chitosan-GP/blood implants leads to a porous subchondral bone structure with well vascularized marrow cavities, that could promote more effective cartilage repair .
Histology of the repair tissue did not show any changes in the number of cells per field, and macrophages and polymorphonuclear cells were not detected, indicating that the implanted chitosan-GP did not evoke an important inflammatory reaction, while permitting cell proliferation. These cells were able to synthesize type II collagen and PGs, suggesting its "Chondrocyte" nature. Nevertheless, the cell population in healing tissues, both in presence of chitosan-GP and in untreated controls, were heterogeneous: only ~40% of the cells were type II collagen-positives and some presented a fibroblastic aspect under light microscopy. A histological scoring system, as well as staining with Safranin-O, Toluidine Blue, and use of polarized microscopy for collagen could be useful to further characterize the healing tissues. However, tissue fragments were differently processed for histology, immunofluorescence, and proteoglycan synthesis under tissue culture conditions, leaving not enough material left for the above mentioned analyses.
Moreover, the PGs synthesized in presence of chitosan-GP were similar to those synthesized in healing tissue without implant, and also to normal cartilage, except that higher proportions of PGs were found in the culture medium of repair tissues. This suggests that the extracellular matrix of the newly synthesized tissue is less dense, in agreement with the findings on type II collagen labelling (see Figures 2 and 4). Chitosan-GP in horses did not increase the PG synthesis rate, although the specific activity of 35S-PGs was slightly increased (difference not statistically significant, Figure 5). This is also in agreement with previously reported data on chondrocytes cultured on chitosan-chondroitin sulphate complexes , which produced equal to control amounts of PGs and type II collagen. Nevertheless, the specific activity of 35S-PGs varied among different animals. This is possibly due to the variations in the number of PG-synthesizing cells in each sample.
It is worth mentioning that these results are related to the osteochondral defect model here employed. In the equine species, the relevance of this model resides in the high prevalence of osteochondral lesions, both acquired or inherited ,. Furthermore, the choice of the depth of the articular cartilage defect has great impact in the tissue response. Osteochondral defects, as employed in the present study, span the entire depth of articular cartilage and penetrate subchondral bone marrow, creating an access to blood cells, macrophages, mesenchymal cells and soluble factors . Osteochondral defects exhibited a rapid cellular response, as opposed to chondral defects, which exhibited a minor healing response, with little cell infiltrates . It is also important to mention that both models of defect design – chondral and osteochondral – are relevant for equines , as well as for other species ,, and the choice to use one or the other must be made judiciously.
Despite extensive research on articular cartilage healing during the last decades, successful repair of damaged cartilage has not been fully achieved. While many new techniques have recently emerged and demonstrated promising results in experimental models, few have exhibited long-term clinical efficacy. Tissue engineering has recently emerged as an interdisciplinary topic, using in vitro cultured cells and tissues, together with artificial implants. Our findings on chitosan-GP suggest that it may be well suitable as a biomaterial for cartilage repair  that could also be used in drug and/or cell delivery . Future studies using in vitro cultured chondrocytes will explore this potential.
aCat #9012-76-4, 419419, Sigma-Aldrich, MO, USA;
bCat #55076-41-1, Sigma-Aldrich, MO, USA;
cCat# 600-401-104-0, Rockland, USA;
dCat# A9647, Sigma, MO, USA;
eDako, Carpinteria, CA, USA;
fVector Laboratories, Inc, Burlingame, CA, USA;
gIPEN-CNEM, São Paulo, SP, Brazil;
hSigma-Aldrich Chemical Co. Inc, Milwaukee, WI, USA;
iScanner CS-9000, Shimadzu;
jPackard Instruments Company Inc., Downers Grove, IL, USA.
LCLCS designed the study and was responsible for obtaining funds. LCLCS and EANM performed all the arthroscopies. EANM and RYAB collected tissue samples and conducted the experimental analysis. RYAB performed the metabolic labelling, isolation, and characterization of proteoglycans, under the supervision of YMM, and participated in the writing and revision of the manuscript. YMM designed and supervised the studies on cartilage proteoglycans, and wrote the manuscript. BC performed the histological analysis. All authors read and approved the final manuscript.
- H & E:
Hematoxylin and eosin
Phosphate buffering saline
Temeroff JS, Mikos AG: Review: tissue engeneering for regeneration of articular cartilage. Biomaterials. 2000, 21: 431-440. 10.1016/S0142-9612(99)00213-6.
Lynn AK, Brooks RA, Bonfield W, Rushton N: Repair of defects in articular joints. J Bone Joint Surg Am. 2004, 86: 1093-1099. 10.1302/0301-620X.86B8.15609.
Beris AE, Lykissas MG, Papageorgiou CD, Georgoulis AD: Advances in articular cartilage repair. Injury. 2005, 36: 14-23. 10.1016/j.injury.2005.10.007.
Grande DA, Southerland SS, Manji R, Pate DW, Schwartz RE, Lucas PA: Repair of articular cartilage defects using mesenchymal stem cells. Tissue Eng. 1995, 1: 345-353. 10.1089/ten.1995.1.345.
Caplan AI, Correa D: The MSC: an injury drugstore. Cell Stem Cell. 2011, 9: 11-15. 10.1016/j.stem.2011.06.008.
Garg T, Singh O, Arora S, Murthy R: Scaffold: a novel carrier for cell and drug delivery. Crit Rev Ther Drug Carrier Syst. 2012, 29: 1-63. 10.1615/CritRevTherDrugCarrierSyst.v29.i1.10.
Wenstrup RJ, Florer JB, Brunskill EW, Bell SM, Chervoneva I, Birk DE: Type V collagen controls the initiation of collagen fibril assembly. J Biol Chem. 2004, 279: 53331-53337. 10.1074/jbc.M409622200.
Martel-Pelletier J, Boileau C, Pelletier JP, Roughley PJ: Cartilage in normal and osteoarthritis conditions. Best Pract Res Clin Rheumatol. 2008, 22: 351-384. 10.1016/j.berh.2008.02.001.
Roughley PJ, Lee ER: Cartilage proteoglycans: structure and potential functions. Microsc Res Tech. 1994, 28: 385-397. 10.1002/jemt.1070280505.
Michelacci YM, Mourão PAS, Laredo-Filho J, Dietrich CP: Chondroitin sulfates and proteoglycans from normal and arthrosic human cartilages. Connect Tissue Res. 1979, 7: 29-36. 10.3109/03008207909152350.
Mourão PAS, Michelacci YM, Toledo OMS: Glycosaminoglycans and proteoglycans of normal and tumoral cartilages of humans and rats. Cancer Res. 1979, 39: 2802-2806.
Kate Y, Gospodarowicz D: Effect of exogenous extracellular matrices on proteoglycan synthesis by cultured rabbit costal chondrocytes. J Cell Biol. 1985, I00: 486-495. 10.1083/jcb.100.2.486.
Pingguan-Murphy B, Lee DA, Bader DL, Knight MM: Activation of chondrocytes calcium signalling by dynamic compression is independent of number of cycles. Arch Biochem Biophys. 2005, 444: 45-51. 10.1016/j.abb.2005.09.015.
Francis Suh J-K, Matthew HWT: Application of chitosan-based polysaccjaride biomaterials in cartilage tissue engineering: a review. Biomaterials. 2000, 21: 2589-2598. 10.1016/S0142-9612(00)00126-5.
Hoemann CD, Sun J, Légaré A, McKee MD, Buschmann MD: Tissue engineering of cartilage using an injectable and adhesive chitosan-based cell-delivery vehicle. Osteoarthritis Cartilage. 2004, 13: 318-329. 10.1016/j.joca.2004.12.001.
Choa JH, Kim S-H, Park KD, Jung MC, Yang WI, Han SW, Noh JY, Lee JW: Chondrogenic differentiation of human mesenchymal stem cells using a thermosensitive poly (N-isopropylacrylamide) and water-soluble chitosan copolymer. Biomaterials. 2004, 25: 5743-5751. 10.1016/j.biomaterials.2004.01.051.
Chen J-P, Cheng T-H: Thermo-responsive chitosan-graft-poly (N-isopropylacrylamide) injectable hydrogel for cultivation of chondrocytes and meniscus cells. Macromol Biosci. 2006, 6: 1026-1039. 10.1002/mabi.200600142.
Chenite A, Chaput C, Wang D, Combes C, Buschmann MD, Hoemann CD, Leroux JC, Atkinson BL, Binette F, Selmani A: Novel injectable neutral solutions of chitosan form biodegradable gels in situ. Biomaterials. 2000, 21: 2155-2161. 10.1016/S0142-9612(00)00116-2.
Hoemann CD, Sun J, McKee MD, Chevrier A, Rossomacha E, Rivard G-E, Hurtig M, Buschmann MD: Chitosan-glycerol phosphate/blood implants elicit hyaline cartilage repair integrated with porous subchondral bone in microdrilled rabbit defects. Osteoarthritis Cartilage. 2007, 15: 78-89. 10.1016/j.joca.2006.06.015.
Ngoenkam J, Faikrua A, Yasothornsrikul S, Viyoch J: Potential of an injectable chitosan/starch/beta-glycerol phosphate hydrogel for sustaining normal chondrocyte function. Int J Pharm. 2010, 391: 115-124. 10.1016/j.ijpharm.2010.02.028.
Malette WG, Quigley HJ, Gaines RD, Johnson ND, Rainer WG: Chitosan: a new hemostatic. Ann Thorac Surg. 1983, 36: 55-58. 10.1016/S0003-4975(10)60649-2.
Ueno H, Nakamura F, Murakami M, Okumura M, Kadosawa T, Fujinag T: Evaluation effects of chitosan for the extracellular matrix production by fibroblasts and the growth factors production by macrophages. Biomaterials. 2001, 22: 2125-2130. 10.1016/S0142-9612(00)00401-4.
Sampaio LO, Bayliss MT, Hardingham TE, Muir H: Dermatan sulfate proteoglycan from human articular cartilage. Variation in its contents with age and structural comparison with a small chondroitin sulfate proteoglycan from pig laryngeal cartilage. Biochem J. 1988, 254: 757-764.
Berto AGA, Sampaio LO, Franco CRC, Cesar RM JR, Michelacci YM: A comparative analysis of structure and spatial distribution of decorin in human leiomyoma and normal myometrium. Biochim Biophys Acta. 2003, 1619: 98-112. 10.1016/S0304-4165(02)00446-4.
Martins SAR, Campos MSQ, Berto AGA, Aguiar JAK, Michelacci YM: Proteoglycan synthesis by human corneal explants submitted to laser in situ keratomileusis (LASIK). Mol Vis. 2007, 13: 142-150.
de Lima CR, dos Santos-Junior JA, Nazário ACP, Michelacci YM: Changes in glycosaminoglycans and proteoglycans of normal breast and fibroadenoma during the menstrual cycle. Biochim Biophys Acta. 1820, 2012: 1009-1019.
Dietrich CP, Dietrich SMC: Eletrophoretic behaviour of acidic mucopolysaccharides in diamine buffers. Anal Biochem. 1976, 70: 645-647. 10.1016/0003-2697(76)90496-6.
Denuziere A, Ferrier D, Damour O, Domard A: Chitosan-chondroitin sulfate and chitosan-hyaluronate polyelectrolyte complexes: biological properties. Biomaterials. 1998, 19: 1275-1285. 10.1016/S0142-9612(98)00036-2.
Hamilton V, Yuan Y, Rigney DA, Puckett AD, Ong JL, Yang Y, Elder SH, Bumgardner JD: Characterization if chitosan films and effects on fibroblast cell attachment and proliferation. J Mater Sci Mater Med. 2006, 17: 469-485. 10.1007/s10856-006-0613-9.
Abarrategi A, Lópiz-Morales Y, Ramos V, Civantos A, López-Durán L, Marco F, López-Lacomba JL: Chitosan scaffolds for osteochondral tissue regeneration. J Biomed Mater Res A. 2010, 95: 1132-1141. 10.1002/jbm.a.32912.
Lavertu M, Filion D, Buschmann MD: Heat-induced transfer of protons from chitosan to glycerol phosphate produces chitosan precipitation and gelation. Biomacromolecules. 2008, 9: 640-650. 10.1021/bm700745d.
Hunziker EB: Articular cartilage repair: basic science and clinical progress. A review of the current status and prospects. Osteoarthritis Cartilage. 2001, 10: 432-463. 10.1053/joca.2002.0801.
Bertolo A, Mehr M, Aebli N, Baur M, Ferguson SJ, Stoyanov JV: Influence of different commercial scaffolds on the in vitro differentiation of human mesenchymal stem cells to nucleus pulposus-like cells. Eur Spine J. 2012, 21 (Suppl 6): 826-838. 10.1007/s00586-011-1975-3.
Onishi H, Machida Y: Biodegradation and distribution of water-soluble chitosan in mice. Biomaterials. 1999, 20: 175-182. 10.1016/S0142-9612(98)00159-8.
Peluso G, Petillo O, Ranieri M, Santin M, Ambrosio L, Calabro D, Avallone B, Balsamo G: Chitosan-mediated stimulation of macrophage function. Biomaterials. 1994, 15: 1215-1220. 10.1016/0142-9612(94)90272-0.
Usami Y, Okamoto Y, Minami S, Matsuhashi A, Kumazawa NH, Tanioka S, Shigemasa Y: Migration of canine neutrophils to chitin and chitosan. J Vet Med Sci. 1994, 56: 1215-1216. 10.1292/jvms.56.1215.
Usami Y, Okamoto Y, Takayama T, Shigemasa Y, Minami S: Chitin and chitosan stimulate canine polymorphonuclear cells to release leukotriene B4 and prostaglandin E2. J Biomed Mater Res. 1998, 42: 517-522. 10.1002/(SICI)1097-4636(19981215)42:4<517::AID-JBM6>3.0.CO;2-U.
Chevrier A, Hoemann CD, Sun J, Buschmann MD: Chitosan-glycerol phosphate/blood implants increase cell recruitment, transient vascularization and subchondral bone remodeling in drilled cartilage defects. Osteoarthritis Cartilage. 2006, 15: 316-327. 10.1016/j.joca.2006.08.007.
Barr ED, Pinchbeck GL, Clegg PD, Boyde A, Riggs CM: Post mortem evaluation of palmar osteochondral disease (traumatic osteochondrosis) of the metacarpo/metatarsophalangeal joint in thoroughbred racehorses. Equine Vet J. 2009, 41: 366-371. 10.2746/042516409X368372.
Van Grevenhof EM, Ducro BJ, Van Weeren PR, Van Tartwijk JM, Van den Belt AJ, Bijma P: Prevalence of various radiographic manifestations of osteochondrosis and their correlations between and within joints in dutch warmblood horses. Equine Vet J. 2009, 41: 11-16. 10.2746/042516408X334794.
Hunziker EB: Articular cartilage repair: are the intrinsic biological constraints undermining this process insuperable?. Osteoarthritis Cartilage. 1999, 7: 15-28. 10.1053/joca.1998.0159.
Shortkroff S, Barone L, Hsu HP, Wrenn C, Gagne T, Chi T, Breinan H, Minas T, Sledge CB, Tubo R, Spector M: Healing of chondral and osteochondral defects in a canine model: the role of cultured chondrocytes in regeneration of articular cartilage. Biomaterials. 1996, 17: 147-154. 10.1016/0142-9612(96)85759-0.
Frisbie DD, Morisset S, Ho CP, Rodkey WG, Steadman JR, McIlwraith CW: Effects of calcified cartilage on healing of chondral defects treated with microfracture in horses. Am J Sports Med. 2006, 34: 1824-1831. 10.1177/0363546506289882.
Frisbie DD, Lu Y, Kawcak CE, DiCarlo EF, Binette F, McIlwraith CW: In vivo evaluation of autologous cartilage fragment-loaded scaffolds implanted into equine articular defects and compared with autologous chondrocyte implantation. Am J Sports Med. 2009, 37 (Suppl 1): 71S-80S. 10.1177/0363546509348478.
Vacanti CA, Langer R, Schloo B, Vacanti JP: Synthetic polymers seeded with chondrocytes provide a template for new cartilage formation. Plast Reconstr Surg. 1991, 88: 753-759. 10.1097/00006534-199111000-00001.
Brittberg M, Lindahl A, Nilsson A, Ohlsson C, Isaksson O, Peterson L: Treatment of deep cartilage defects in the knee with autologous chondrocyte transplantation. N Engl J Med. 1994, 331: 889-895. 10.1056/NEJM199410063311401.
The authors want to express their gratitude to Dr. Maria Gabriela N. Campos, Faculdade de Engenharia Qu mica, UNICAMP, Campinas, SP, Brazil, for the preparation of chitosan-GP; to Dr. Tha's S.L. Machado, for noteworthy help in some of the experiments on proteoglycan isolation and characterization; and to Prof. Dr. Maria Lucia Z. Dagli, Departamento de Patologia Animal, FMVZ-USP, São Paulo, SP, Brazil, for histological analysis.
This research was supported by Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq), Brasília, DF, Brazil; Fundação Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES), Brasília, SP, Brazil; and Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP), São Paulo, SP, Brazil. These sponsors did not have any influence on the study design, on the collection, analysis and interpretation of data, or on the writing of the manuscript and decision to submit for publication.
The authors declare that they have no competing interests.
Authors’ original submitted files for images
About this article
Cite this article
Martins, E.A., Michelacci, Y.M., Baccarin, R.Y. et al. Evaluation of chitosan-GP hydrogel biocompatibility in osteochondral defects: an experimental approach. BMC Vet Res 10, 197 (2014) doi:10.1186/s12917-014-0197-4
- Type II collagen
- Equine joint